Regufoam Vibration Isolation

Regufoam® vibration is an elastic polyurethane foam designed for optimal vibration isolation. It is available in twelve different densities and various thicknesses, now including thinner options, offering even more flexibility to suit diverse needs.

Regufoam 190

Product Characteristics

Sheets, strips or pads
On request: Die-cutting, water-jet cutting, self-adhesive versions possible

Continuous static load
0.018 N/mm²

Continuous and variable loads/operating load range
0 to 0.028 N/mm²

Peak loads (rare, short-term loads)
0.8 N/mm²

 

Standard forms of delivery, ex warehouse

Rolls
Thickness: 12.5 and 25 mm are standard, and regularly available off the shelf. Special thicknesses on request
Length: 5000 mm, special lengths available on request
Width: 1500 mm

On request we can tailer to your needs and produce 75, 50, 37.5, 25, 12.5, 6 mm all the way down to 2 mm thicknesses.

Technical Specifications

regufoam-190-specifications.xlsx

Regufoam 190

Physical property Norm Result Comment
Static modulus of elasticity Based on EN 826 0.10 - 0.25 N/mm2 Tangential modulus, see figure “modulus of elasticity”
Dynamic modulus of elasticity Based on DIN 53513 0.25 - 0.55 N/mm2 Depending on frequency, load and thickness, see fi gure “dynamic stiffness“
Mechanical loss factor DIN 53513 0.25 Load-, amplitude- and frequency-dependent
Compression set Based on DIN EN ISO 1856 2.0 % Measured 30 minutes after decompression with 50 % deformation / 23 °C after 72 hrs
Tensile strength Based on DIN EN ISO 1798 0.4 N/mm2
Elongation at break Based on DIN EN ISO 1798 220%
Tear resistance Based on DIN ISO 34-1 2.0 N/mm
Fire behaviour DIN 4102 B2
DIN EN 13501-1 E
Sliding friction REGUPOL-laboratory 0.7 Steel (dry)
REGUPOL-laboratory 0.8 Concrete (dry)
Compression hardness Based on DIN EN ISO 3386-2 22 kPa Compressive stress at 25 % deformation test specimen h = 25 mm
Rebound elasticity Based on DIN EN ISO 8307 35% dependent on thickness, test specimen h = 25 mm
Force reduction DIN EN 14904 61% dependent on thickness, test specimen h = 25 mm